13 февр. 2018 г. · The way to harden 304 is to roll it thinner; there is no heat treatment available. This is something learned in first year mechanical ... How to avoid work hardening 304 while machining Does hardened 300-series stainless exist or not? Need 1/16 ... Другие результаты с сайта www.practicalmachinist.com

17 мар. 2003 г. · Take the 304 ball and shot-peen it. If the surface roughness is acceptable, the deformations will harden the surface.

11 окт. 2023 г. · Yes, 304 SS material can be made hard by hardening processes such as cold working or heat treating. Hardening processes increase the hardness ... Can 304 stainless steel be heat treated? - Quora If stainless steel cannot be hardened, will it still be ... - Quora Другие результаты с сайта www.quora.com

20 июл. 2015 г. · 304 can be hardened by the process of cold working. However, you probably want to buy the material pre hardened (just google 304 SS half hard) ...

304 is an austenitic stainless steel. You can't through-harden it. You might be able to nitride it, but this will probably create more problems than it is ...

The only way 304 hardens easily is work hardening, like when you push on it with a dull drill bit. So if you need a hard pin, use a steel with some carbon in it ...

30 мая 2016 г. · Cold rolling or cold forging is the only way to harden 304. It is considered a non hardenable steel. With a certain % of reduction, it will harden some.

20 мар. 2022 г. · Quenching, carburizing, nitriding and other processes can be used. Quenching and tempering can improve overall properties, including hardness.

304/304L is not hardenable by heat treatment. Cold working increases tensile strength and hardness. Annealing range is between 1850° and 2050°F. Cool rapidly.